Hybond838 High Performance Instant Cyanoacrylate Adhesive

                Hybond838 High Performance Instant Cyanoacrylate Adhesive
                                                 from Shirley(hengying@cnhybond.com  0086-18927302778  Skype:hengying11)

1. Color: Transparent. 

2. Product Information 
838 Department of the British Constant surface-sensitive α-cyanoacrylate instant adhesives. 

It is through the special treatment, synthetic made of a high-performance Instant Adhesive
Fast setting, low viscosity ethyl based Powerful adhesive.

Applied to shoes, magnetic, glass, metal, stone and other materials

3. Typical uses 
it is most suitable for wood, sculpture, magnetic, glass, metal, stone, leather, wood and other materials. It owns such sound features as high strength.

4. Features 
The chemical composition of base material:  cyanoacrylate 

Appearance:  Transparent
Viscosity (25 ℃, mpa.s): 2-6cps
Time for the beginning of solid (S): -3-8
Shear strength (Mpa): ≥ 27 

Tensile shear strength(kgf/cm2) ≥90
Flash Point (℃) ---------> 80
Fill the largest gap (mm )---- 0.1
Operating temperature (℃ )------- 54 ~ 83 

Shelf time: (5℃)12month

5. Caution 
(1). Coated should be clean, dry no grease, choice of cleaning agent 7010, the better.
(2). 838 instant adhesive will be in a surface (also have two surface coating).
(3). Compress the two surfaces close up, 10 seconds early curing, 1 minute to reach the initial intensity, in the majority of bonding material on the strength required to achieve 12 ~ 24 hours.
(4). This product is cyanoacrylate, quickly stick to skin and eyes. Once the skin of the spilled materials

Hybond 828 High Performance Cyanoacrylate Adhesive (Glue)

            Hybond 828 High Performance Cyanoacrylate Adhesive (Glue)
                                 from Shirley(hengying@cnhybond.com   0086-18927302778  Skype:hengying11)

Transparent 

It is made from the special treatment, synthetic made of a high-performance instant adhesive.
It is a fast setting, low viscosity ethyl based powerful adhesive.

It can be applied to lots kinds of shoes: Applied to magnetic, glass, metal, stone and other materials.

Product Introductions:

828 is Department of the British Constant surface-sensitive α-cyanoacrylate instant adhesives. 

Typical uses: 

It is most suitable for wood, sculpture, magnetic, glass, metal, stone, leather, wood and other materials. Also it owns such sound features as high strength.

 Features 
The chemical composition of base material cyanoacrylate Transparent appearance 
Viscosity (25 ℃, mpa.s )---- 2-5cps 
Time for the beginning of solid (S )-------3-8
Shear strength (Mpa )------- ≥ 27 

Tensile shear strength(kgf/cm2) ≥90
Flash Point (℃) ---------> 80 
Fill the largest gap (mm )---- 0.1 
Operating temperature (℃ )------- 54 ~ 83 

Shelf time: (5℃) 12months.

Caution:  
• Coated should be clean, dry no grease, choice of cleaning agent 7010, the better. 
• 828 instant adhesive will be in a surface (also have two surface coating). 
• Compress the two surfaces close up, 10 seconds early curing, 1 minute to reach the initial intensity, in the majority of bonding material on the strength required to achieve 12 ~ 24 hours. 
• This product is cyanoacrylate, quickly stick to skin and eyes. Once the skin of the spilled materials

Hybond319 Instant Adhesive

                       Hybond319 Instant Adhesive
                                                  from Shirley(hengying@cnhybond.com  0086-18927302778  Skype:hengying11)

Product description

CNHYBOND 319  provides the following product 

Characteristics:

Technology:   acrylic

Chemical Type:   Modified acrylic ester

Appearance(uncured): clear light amber liquid

Components:    One component-requires no mixing

Viscosity:       Medium

Cure:           Anaerobic with acivator

Application:      Bonding

Strength:          High

CNHYBOND 319 typical applications include bonding materials such as metals,glass,ceramics or plastics, the product cures when confined between close fitting parts with the aid of activator 7649

TYPICAL  PROPERTIES OF UNCURED MATERIAL

Specific Gravity@25℃           1.11

Viscosity,Brookfield-RTV, 25℃,MPa.s(cp)

Spindle 4,speed 20 rpm                          1500 to 4000

TYPICAL PERFORMANCE OF CURED MATERIAL 

Physical properties

Coefficient of thermal conductivity,iso8302 w/(m.k):        0.1

Specific Heat,kj/(kg.k)                                 0.3

Adhesive Properties

After 1 hours@22℃,Activator 7649 on 2 sides 

Lap shear strength  iso4587                                 

Steel(gritblasted)                                      N/mm2  >=10.3

After 1 hours@22℃,Activator 7649 on 2 sides 

Lap shear strength  iso4587                                 

Steel(grit blasted):)

0.25mm gap                                          N/mm2>=4.5

Directions for use:

For Assembly

1:For best results, clean bond surfaces 

2:to ensure a fast and reliable cure,activator 7649  should be applied to one of the bond surfaces and the adhesive to the other surface,parts should be assembled within 15 minutes

3:the recommended bondline gap is 0.1mm ,where bond gaps are large(up to a maximum of 0.5mm),or faster cure speed is required activator 7649 should be applied to both surfaces ,parts should be assembled immediately(within 1 minute)

4: Excess adhesive can be wiped away with organic solvent 

5:Bond should be held clamped until adhesive has fixtured

6:product should be allowed to develop full strength befor subjecting to any servie loads(typically 24 to 72 hours

Optimal Storage:8℃ to 21°,store product in the unopened container in a dry location.

NOTE:

The data contained herein are furnished for information only and are believed to be reliable.We cannot assume responsibility for ther results obtained by others over whose methods we have no control.it is ther user,s responsibility to determine suitability for the user,s purpose of any production methods mentioned herein and to adopt such precautions as many be advisable for the protection of property and of persons against any hazards that may be involved in the handling and use thereof.

Hybond 496 General Purpose Methyl Cyanoacrylate Bonding Adhesive

             Hybond 496 General Purpose Methyl Cyanoacrylate Bonding Adhesive 

                                                     from Shirley(hengying@cnhybond.com   0086-18927302778  Skype:hengying11)


Product Description 

HYBOND 496 is a general purpose cyanoacrylate instant adhesive. It is particularly suited to bonding of metal substrates

Product Characteristics 

Technology	Cyanoacrylate
Chemical Type	Ethyl cyanoacrylate
Appearance (uncured)	Transparent colorless liquid
Components	one part-require no mixing
Viscosity,Brookfield-LVF,25℃1              Spindle 1, speed 30 rpm	40-60cps
Cure	Humidity
Application	Bonding
Key substrates	Metals, plastics and Elastomers
Specific Gravity@25℃:	1.1

Typical Curing Performance 

Under normal conditions, the atmospheric moisture initiates the curing process. Although full functional strength is developed in a relatively short time, curing continues for at least 24 hours before full chemical/solvent resistance is developed.

Cure Speed vs. Substrate

The rate of cure will depend on the substrate used. The table below shows the fixture time achieved on different materials at 22 °C / 50 % relative humidity. This is defined as the time to develop shear strength of 0.1 N/mm².

Fixture Time, seconds:

Mild Steel (degreased)	20 to 40
Aluminum	30 to 60
Zinc dichromate	30 to 60
Neoprene	<10
Rubber, nitrile	<10
ABS	10 to 30
PVC	30 to 70
Polycarbonate	20 to 70
Phenolic	10 to 30

Cure Speed vs. Bond Gap

The rate of cure will depend on the bondline gap. Thin bond lines result in high cure speeds, increasing the bond gap will decrease the rate of cure.

Cure Speed vs. Humidity

The rate of cure will depend on the ambient relative humidity. Higher relative humidity levels result in more rapid speed of cure.

Cure Speed vs. Activator

Where cure speed is unacceptably long due to large gaps, applying activator to the surface will improve cure speed. However, it can reduce ultimate strength of the bond effect.

Directions for use:

(1). Bond areas should be clean and free from grease. Clean all surfaces with a HYBOND cleaning solvent and allow to be dried.

(2). HYBOND Primer may be applied to the bond area. Avoid applying excess Primer. Allow the Primer to dry.

(3). HYBOND Activator may be used if necessary. Apply HYBOND Activator to one bond surface (do not apply activator to the primed surface where Primer is also used). Allow the Activator to dry 

(4). Apply adhesive to one of the bond surfaces (do not apply the adhesive to the activated surface). Do not use items like tissue or a brush to spread the adhesive. Assemble the parts within a few seconds. The parts should be accurately located, as the short fixture time leaves little opportunity for adjustment.

(5). HYBOND Activator can be used to cure fillets of product outside the bond area. Spray or drop the activator on the excess product.

(6). Bonds should be held fixed or clamped until adhesive has fixtured.

(7). Product should be allowed to develop full strength before subjecting to any service loads (typically 24 to 72 hours after assembly, depending on bond gap, materials and ambient conditions).

Storage

Store product in the unopened container in a dry location, storage instruction is shown on the label of bottle

Optimal Storage: 2 °C to 8 °C. Storage below 2 °C or greater than 8 °C can adversely affect product properties. Material removed from containers may be contaminated during use. Do not return product to the original container. Heng ying Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated. If additional information is required, please contact us.

Hybond 495 Super Bonder Instant Adhesive

             Hybond 495 Super Bonder Instant Adhesive
                                    from Shirley(hengying@cnhybond.com  0086-18927302778  Skype:hengying11)

1. Product Description 

HYBOND 495 is a general purpose, medium viscosity cyanoacrylate instant adhesive.

Application: bonding rubber, metal and plastics, max. gap fill up to 0.1mm

2. Product Characteristics 

Technology	Cyanoacrylate
Chemical Type	Ethyl cyanoacrylate
Appearance (uncured)	Transparent colorless liquid
Components	one part-require no mixing
Viscosity,Brookfield-LVF,25℃1              Spindle 1, speed 30 rpm	40-60cps
Cure	Humidity
Application	Bonding
Key bstrates	Metals, plastics and Elastomers
Specific Gravity@25℃:	1.5

3. Typical Curing Performance 

Under normal conditions, the atmospheric moisture initiates the curing process. Although full functional strength is developed in a relatively short time, curing continues for at least 24 hours before full chemical/solvent resistance is developed.

4. Cure Speed vs. Substrate

The rate of cure will depend on the substrate used. The table below shows the fixture time achieved on different materials at 22 °C / 50 % relative humidity. This is defined as the time to develop shear strength of 0.1 N/mm².

Fixture Time, ISO 4587, seconds:

Mild Steel (degreased)	10 to 30
Aluminum(degreased)	5 to 15
Zinc dichromate	30 to 90
Neoprene	<5
Rubber, nitrile	<5
ABS	10 to 30
PVC	3 to 10
Polycarbonate	20 to 60
Phenolic	5 to 20

5. Cure Speed vs. Bond Gap

The rate of cure will depend on the bondline gap. Thin bond lines result in high cure speeds, increasing the bond gap will decrease the rate of cure.

6. Cure Speed vs. Humidity

The rate of cure will depend on the ambient relative humidity. Higher relative humidity levels result in more rapid speed of cure.

7. Cure Speed vs. Activator

Where cure speed is unacceptably long due to large gaps, applying activator to the surface will improve cure speed. However, it can reduce ultimate strength of the bond effect.

8. Directions for use:

(1). Bond areas should be clean and free from grease. Clean all surfaces with a HYBOND cleaning solvent and allow to be dried.

(2). HYBOND Primer may be applied to the bond area. Avoid applying excess Primer. Allow the Primer to dry.

(3). HYBOND Activator may be used if necessary. Apply HYBOND Activator to one bond surface (do not apply activator to the primed surface where Primer is also used). Allow the Activator to dry 

(4). Apply adhesive to one of the bond surfaces (do not apply the adhesive to the activated surface). Do not use items like tissue or a brush to spread the adhesive. Assemble the parts within a few seconds. The parts should be accurately located, as the short fixture time leaves little opportunity for adjustment.

(5). HYBOND Activator can be used to cure fillets of product outside the bond area. Spray or drop the activator on the excess product.

(6). Bonds should be held fixed or clamped until adhesive has fixtured.

(7). Product should be allowed to develop full strength before subjecting to any service loads (typically 24 to 72 hours after assembly, depending on bond gap, materials and ambient conditions).

9.Storage

Store product in the unopened container in a dry location, storage instruction is shown on the label of bottle

Optimal Storage: 2 °C to 8 °C. Storage below 2 °C or greater than 8 °C can adversely affect product properties. Material removed from containers may be contaminated during use. Do not return product to the original container. Heng ying Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated. If additional information is required, please contact us.

10.Note

The data contained herein are furnished for information only and are believed to be reliable. We cannot assume responsibility for the results obtained by others over whose methods we have no control. It is the user's responsibility to determine suitability for the user's purpose of any production methods mentioned herein and to adopt such precautions as may be advisable for the protection of property and of person against any hazards that may be involved in the handling and then use. In light of the foregoing, HENG YING Corporation specifically disclaims all warranties expressed or implied, including warranties of merchantability or fitness for a particular purpose, arising from sale or use of HENG YING Corporation’s products. HENG YING Corporation specifically disclaims any liability for consequential or incidental damages of any kind, including lost profits. The discussion of various processes or compositions is not to be interpreted as representation that they are free from domination of patents owned by others or as a license under any HENG YING Corporation patents that may cover such processes or compositions. We recommend that each prospective user test his proposed application before repetitive use, using this data as a guide.